tread steel plate

tread steel plate: 1.Model: 304,316, M2 ,M35,M42, W9 etc 2.Class:Steel plate series 3.Size: available upon customers'

tread steel plate :1.Model: 304,316, M2 ,M35,M42, W9 etc2.Class:Steel plate series

Specifications:1) Size:  sizes available upon customers' requirements2)Standards:    a) ASTM (U.S.A)        A213/A213M (SA213/SA213M)        A269/A269M        A312/A312M (SA312/SA312M)    b) GOST (Russia)    c) JIS (Japan)    d) GB (China)

3) Customized manufacture and OEM available4) Packing:       Knitting bag or wooden cas

5)The detailed material we would offer:

W6Mo5Cr4V2,it is similar to M2(ASTM), S6-5-2(DIN),SKH51(JIS)

Chemical Composition: C 0.85, Si 0.38, Mn 0.35, P≤0.030, S≤0.030, Cr 4.10,W 6.00, Mo 4.80 V 1.85

Annealed Hardness: HB≤255

Heat treatment temp: Hardening 1210-1230   Temperings: 550

Secondary: 63-65 HRC

Application: Be used widely in making all kinds of knives and durable cold working molds.

   2. W6Mo5Cr4V2Co5,it is similar to M35(ASTM), 1.3243(DIN),SKH35(JIS)

Chemical Composition: C 0.93, Si 0.38, Mn 0.35, P≤0.030, S≤0.030, Cr 4.10,W 6.30, Mo 4.80 V 1.85, Co5.00

Annealed Hardness: HB≤269

Heat treatment temp: Hardening 1200-1220   Temperings: 550

Secondary: 64-67 HRC

Application: Steel for difficult and hi-speed cutting blades, blades which lay particular on durable

    3. W2Mo9Cr4VCo8,it is similar to M42(ASTM), 1.3243(DIN),SKH59(JIS)

Chemical Composition: C 1.10, Si 0.55, Mn 0.35, P≤0.030, S≤0.030, Cr 4.10,W 1.05, Mo 9.50 V 1.05, Co 8.00

Annealed Hardness: HB≤269

Heat treatment temp: Hardening 1210-1230   Temperings: 550

Secondary: 65-67 HRC

Application: Steel for difficult and hi-speed cutting blades, blades which lay particular on toughness

    4. W18Cr4V,it is similar to T1(ASTM), 1.3355(DIN),SKH2(JIS)

Chemical Composition: C 0.75, Si 0.35, Mn 0.35, P≤0.030, S≤0.030, Cr 4.05,W 18,V 1.10

Annealed Hardness: HB≤255

Heat treatment temp: Hardening 1270-1285   Temperings: 560

Secondary: 62-65 HRC

Application: Steel for common cutting blades.

     5. W9Mo3Cr4V

Chemical Composition: C 0.83, Si 0.35, Mn 0.35, P≤0.030, S≤0.030, Cr 4.05,W 8.90, Mo2.90, V 1.45

Annealed Hardness: HB≤255

Heat treatment temp: Hardening 1220-1240   Temperings: 550

Secondary: 63-65 HRC

Application: Chinese material, similar capability to M2

     6. W6Mo5Cr4V2Co(GB),it is similar to M2 modify(ASTM)

Chemical Composition: C 0.80, Si 0.38, Mn 0.35, P≤0.030, S≤0.030, Cr 4.10,W 5.40, Mo4.80 V 2.10, Co≤0.5

Annealed Hardness: HB≤255

Heat treatment temp: Hardening 1200-1220   Temperings: 550

Secondary: 62-64 HRC

Application: Better toughness than M2

tread steel plate